| Lubricants |
- ASTM D-445
Viscosity @40°C: 34.10
- ASTM D-445
Viscosity @100°C: 8.0
- ASTM D-130
Copper Corrosion (150°C for 3.0hrs): 2c
- ASTM D-130
Copper Corrosion (100°C for 3.0hrs): 1a
- ASTM D-97
Pour Point °C: -39
- ASTM D-2783M
Extreme Pressure Four Ball Weld Point (kg): 200
- ASTM D-4172
Four Ball Wear Test, Average Scar Diameter(mm): 0.42
- ASTM D-665A
Rust Preventing Characteristics: Pass
- ASTM D-665B
Synthetic Seawater Corrosion Test: Pass
- ASTM D-943
Oxidation Stability: 60hrs
- ASTM D-92
Flash Point: 250°C
- ASTM D-1401
Emulsion Characteristics
Oil Layer (hazy): 43 ml
Water Layer (clear): 37 ml
Emulsion: 0 ml
Separation Time: < 20 min.
- ASTM D-892
Foam Test
Sequence 1: 75°F, 0 - Foaming Tendency, 0 - Foaming Stability
Sequence 2: 200°F, 60 - Foaming Tendency, 0.020 sec. Foaming Collapse
Sequence 3: 75°F 0 - Foaming Tendency, 0 - Foaming Stability
|
- D 128
Thickener Type: Polyurea
NLGI Consistency Grade: 2
- D 127
Cone Penetration @ 77°F (0.1 mm)
worked 60 strokes: 295
worked 10000 strokes: 348
- Visual
Texture: Smooth
- Visual
Colour: Amber
- D 445
Base Oil Viscosity (centistokes)
@ 40°C: 34.2
@100°C: 7.88
- D 2270
Viscosity Index: 210
- D 1264
Water Washout @ 60°C (% mass loss): 5.3
- D 4049
Water Sprayoff (% mass loss): 33.77
- D 3596
Shell Four Ball EP (kg)
Weld Load: 250
LWI: 45
- D 2509
Timkin OK Load (lbs.): 45
- D 2265
Dropping Point (°F): 530
- D 1743
Rust Prevention: Pass
- D 2266
4 Ball Wear (scar diameter, mm): 0.56
- D 1478
Low Temperature Torque (-40°C, Nm): 12.9
|
|
|
| |
|
|